Product Detail

Epoxy Powder Coating

"Zx-9 Zhenxin ® Epoxy Powder Coating" is a high quality thermosetting epoxy powder coating for corrosion protection of valves and fittings for ductile iron or cast steel substrates.As a sanitary and environmentally friendly coating,ZX-9 Zhenxin ® Epoxy Powder Coating's excellent adhesion to metal extrusion provides long-term protection for the coated components, reliably protecting the function and value of all parts of the ordinary water gas distribution network.


12.jpg

Keyword
powder coating
Brand
Zhenxin Paint
Collect
Explain

PRODUCT DESCRIPTION :

"Zx-9 Zhenxin ® Epoxy Powder Coating" is a high quality thermosetting epoxy powder coating for corrosion protection of valves and fittings for ductile iron or cast steel substrates.As a sanitary and environmentally friendly coating,ZX-9 Zhenxin ® Epoxy Powder Coating's excellent adhesion to metal extrusion provides long-term protection for the coated components, reliably protecting the function and value of all parts of the ordinary water gas distribution network.


POWDER PROPERTIES:

Density (liquid displacement method)                       

1.3-1.7g/cm3

Gel time at 200℃

40-60 sec.


MATERIAL PROPERTIES:

Recommended film thickness

250um-500um

Glossiness (60 degrees Angle gloss meter)

95 degrees

Hardness (Pencil durometer)

2H

Impact resistance (paint film impactor)

8J-10J

Bending resistance (bending tester)

φ3mm

Drawing adhesion (drawing instrument), room temperature

20Mpa

Salt spray test (ISO7253), 800h

Class 1

Cathode Stripping (65 °, 48h, 1.5V)

3mm

Chemical boiling adhesion

grade 1

Interfacial porosity (SY/0315-97)

1

SPRAYING PROCESS:

1Preheat object temperature:220℃-250℃, 40min-60min

2Surface temperature of the coating object: 110℃-140℃ to ensure the thickness of spraying

3Curing object temperature: 190℃-200℃(Effective temperature) 15min-20min

4The surface is free from grease, salt and other impurities

5Sand blasting must be clear of sand, rust and sharp edges

6Sa 2.5, recommended anchorage profile 60um

7Ensure the temperature of preheating process is uniform and stable, avoid reoxidation

8Spraying or fluidization should begin immediately after preheating to complete a single coating process in the shortest possible time.

Copyright @ 2024. All rights reserved.ANHUI ZHENXIN PAINT CO.,LTD .皖ICP备15025806号

Add:XINHE INDUSTRIAL PARK,QINGYANG COUNTY,

CHIZHOU CITY, ANHUI PROVINCE,CHINA



Tel: +86 17756609998

Tel:400-800-3522

Whatsapp: +86 15905660311

E-mail: bob.wu@zhenxintl.com

             qyzxhg@163.com



  • Telephone

    • 400-800-3522
    • bob.wu@zhenxintl.com
Technical Support: 亿网网络 | Admin Login
×
seo seo